Immobilization of self-assembled pre-dispersed nano-TiO2 onto montmorillonite and its photocatalytic activity
Tingting Zhang
,
Yuan Luo
,
Bing Jia
,
Yan Li
,
Lingling Yuan
,
Jiang Yu
DOI:10.1016/j.jes.2015.01.010
Received August 21, 2014,Revised December 02, 2014, Accepted January 14, 2015, Available online April 24, 2015
Volume 27,2015,Pages 108-117
The immobilization of pre-dispersed TiO2 colloids onto the external surface of the clay mineral montmorillonite (Mt) was accomplished and regulated via a self-assembly method employing the cationic surfactant cetyltrimethylammonium bromide (CTAB). The role of CTAB in the synthesis process was investigated by preparing a series of TiO2-CTAB-Mt composites (TCM) with various CTAB doses. The results indicated that a uniform and continuous TiO2 film was deposited on the external surface of montmorillonite in the composite synthesized with 0.1 wt.% of CTAB, and the TCM nano-composites showed much higher values for specific surface area, average pore size and pore volume than the raw montmorillonite clay. Then, the formed TCM materials were applied in photocatalytic degradation of 2,4-dichlorophenol (2,4-DCP) in aqueous solution. The degradation efficiency reached as high as 94.7%. Based on the degradation intermediates benezoquinone, fumaric acid and oxalic acid identified by LC–MS analysis, a mechanism for the photocatalytic oxidation of 2,4-DCP on TiO2/Mt nano-composites is proposed.